SS400 steel is a structural hot rolled steel in the form of plates, sheets and strips for general structural applications. SS400 carbon steel with proper tensile strength and toughness, good plasticity, welding performance and processing property.
The Chemical Composition of SS400 Steels as under:
Carbon (C) is not identified in the standard.
Manganese (Mn) is not identified in the standard.
Maximum percentage of Phosphorous (P) is 0.050 percent.
Maximum percentage of Sulphur (S) is 0.050 percent.
Remaining is iron (Fe) percentage and with few negligible impurities.
Carbon (C) is not identified in the standard.
Manganese (Mn) is not identified in the standard.
Maximum percentage of Phosphorous (P) is 0.050 percent.
Maximum percentage of Sulphur (S) is 0.050 percent.
Remaining is iron (Fe) percentage and with few negligible impurities.
JIS G3101 SS400 Steel Mechanical Properties :
Density: 7860kg/m3
Young’s Modulus: 190-210GPa
Tensile Strength: 400 – 510 MPa
Yield Strength: 205-245 MPa
Poisson’s ratio: 0.26
Hardness Brinell Hardness: 160HB
Density: 7860kg/m3
Young’s Modulus: 190-210GPa
Tensile Strength: 400 – 510 MPa
Yield Strength: 205-245 MPa
Poisson’s ratio: 0.26
Hardness Brinell Hardness: 160HB
SS400 equivalent:
Similar DIN JIS SS400
17100 St 44-2
Equivalent to ASTM JIS SS400
ASTM A36, ASTM A283 Grade D
EN equivalent to JIS SS400
S275 EN / BS 43A
Similar DIN JIS SS400
17100 St 44-2
Equivalent to ASTM JIS SS400
ASTM A36, ASTM A283 Grade D
EN equivalent to JIS SS400
S275 EN / BS 43A
JIS G3101 SS400 carbon steel is popular for proper tensile strength and toughness, good plasticity, welding performance and processing property. SS400 available in sheets, flats, bars, sections, etc. Applied to general structural constructions-bridges and ships, final product always supplied hot rolled.